… extremely wear resistant and
extremely strong
DIAMANT proceramic is a highly filled pastelike 2-component polymer material with highgrade ceramic filler combinations and special massive mini balls with highest wear resistance.
DIAMANT proceramic is mainly used to wear-protect all kinds of materials being exposed to extreme wear by hard particles (in gases, liquids or hard media). DIAMANT proceramic is best also against lateral impacts. Thus, DIAMANT proceramic is also used to replace ceramic tiles.
Properties
- high wear resistance when extremely loaded
- filled with high grade ceramic filllers and special high-wear-resistant massive mini balls
- containers with lose materials
- dripproof
- coat thicknessup to 1 cm per layer possible
- finer grades are tough-elastic
Typical Applications
- extruders, ventilators,
- tubes (especially down pipes, chutes,
- container for lose goods
- exhaust systems (temperature limit),
- centrifuges, cyclones,
- transport systems, incl. screw conveyors
- all typen of mixers (container, mixer)
Pack Sizes
- 100g, 250g, 500g, 1.000g
- large packs on requeste
Technical Data:
- Thermal Resistance
permanently to 150°C
peak 200°C - Pot Life
at 5°C approx. 3 hours - Cure Time
24 hours (full load = 48 hours)
| Typ | Product- No. |
Properties | E-Modulus [N/mm²] |
Spec. Weight [g/cm3] |
Compressive- Strength [N/mm²] |
Hardness [Shore D] |
| 1913 FL/P semifluid | 1913 | soft paste | 4800 | 2,1 | 105 | >85 |
| 1914 P = Paste | 1914 | Paste | 5400 | 2,1 | 110 | >85 |
| 1867 P = Paste | 1867 | Paste | 4800 | 2,1 | 101 | >85 |
| 1933 P = Paste | 1933 | Paste | 5400 | 2,1 | 115 | >85 |
| 1934 P = Paste | 1934 | Paste | 6000 | 2,1 | 115 | >85 |
| 1976 P = Paste | 1976 | Paste | 4800 | 2,1 | 105 | >85 |
All material values are average values and may vary on ground of volumes and ambient conditions. These values are based on standard conditions (STP) of 20°C (273°K) and 1013mbar.